高强度齿轮20CrMnTi的热处理工艺编制
摘要：本文重点对20CrMnTi高强度齿轮钢的性能、热处理工艺及其质量检验进行讨论。在本文不仅描述了20CrMnTi的化学成分及其对齿轮组织结构和性能的影响，还介绍了常规的热处理工艺。通过对20CrMnTi高强度齿轮钢热处理工艺路线的分析，采用正火和调质的热处理方式，并在热处理过程中采用合理的预防措施防止齿轮产生缺陷，使材料具备良好的综合力学性能并符合各项标准，从而满足齿轮的使用性能要求。
关键词：高强度齿轮；20CrMnTi；热处理工艺；缺陷
Preparation of the heat treatment technic of high strength gear 20CrMnTi
Abstract：This paper focuses on the 20CrMnTi high strength gear process and the quality of the performance test, heat treatment was discussed. In this paper not only describes the chemical composition of 20CrMnTi and its effect on the structure and properties of gear organization, also introduced the conventional heat treatment process. Through the analysis of 20CrMnTi high strength gear just heat treatment process, heat treatment and quenching and tempering by, and in the process of adopting reasonable precautions to prevent gear defects, make the materials with comprehensive and good mechanical properties and conform to the standard, so as to meet the requirements of the use of the performance of gear.
Keywords: High strength gear，20CrMnTi，Heat treatment process，Defect
目录
一、引言· 7
二、前言· 7
（一）齿轮的发展史· 7
（二）20CrMnTi简介· 8
（三）研究的目的和意义· 8
三、方案· 9
（一）原材料的选择· 9
（二）齿轮的性能要求· 9
1. 满足齿轮材料的机械性能· 9
2. 满足齿轮材料的工艺性能· 9
3. 满足齿轮材料经济性能· 10
四、热处理· 10
（一）预备热处理· 10
（二）调质· 11
五、渗碳热处理工艺· 11
（一）钢的化学成分· 12
（二）渗碳工艺· 13
六、淬火低温回火· 13
(一) 淬火· 13
(二) 低温回火· 13
七、热处理后的金相组织· 14
(一) 20CrMnTi等温正火后金相组织· 14
(二) 20CrMnTi经渗碳后淬火、回火处理金相组织· 14
八、质量控制与检验方法· 16
(一) 随炉试样检验· 16
(二) 齿轮热处理质量检验· 19
九、热处理工艺过程中的质量检验· 19
(一) 渗碳淬火后齿轮的检验项目、内容和要求· 19
(二) 渗碳齿轮的常见缺陷及防止措施· 20
(三) 渗碳淬火后畸变原因分析及解决措施· 22
十、结论· 27
参考文献· 28
参考文献：
【1】彭福泉主编，金属材料实用手册，机械工业出版社，1987年
【2】河北工学院王健安主编，金属学与热处理下册热加工专业用，机械工业出版社，1980年
【3】中国机械工程学会热处理专业学会《热处理手册》编委会编，热处理手册第2版第二卷典型零件的热处理，机械工业出版社，1991年
【4】夏立芳编，金属热处理工艺学修订版，哈尔滨工业大学出版社，2008年
【5】热处理工艺学，机械工业出版社， 1988
【6】陆兴热，处理工程基础，北京：机械工业出版社，1997(3),30-36
【7】刘瑞堂，机械零件失效分析，哈尔滨：哈尔滨工业大学出版社，2005
【8】张太昌，齿轮检测500问，北京中国标准出版社，2007
【9】金荣植，齿轮的热处理畸变、裂纹与控制方法，机械工业出版社2014
【10】那顺桑，金属热处理300问，北京工业出版社2007
【11】金荣植，齿轮热处理常见缺陷分析与对策，化学工业出版社2014
【12】吉泽升，热处理炉，哈尔冰工业大学出版社2010
http://www.bysj580.com/
摘要：本文重点对20CrMnTi高强度齿轮钢的性能、热处理工艺及其质量检验进行讨论。在本文不仅描述了20CrMnTi的化学成分及其对齿轮组织结构和性能的影响，还介绍了常规的热处理工艺。通过对20CrMnTi高强度齿轮钢热处理工艺路线的分析，采用正火和调质的热处理方式，并在热处理过程中采用合理的预防措施防止齿轮产生缺陷，使材料具备良好的综合力学性能并符合各项标准，从而满足齿轮的使用性能要求。
关键词：高强度齿轮；20CrMnTi；热处理工艺；缺陷
Preparation of the heat treatment technic of high strength gear 20CrMnTi
Abstract：This paper focuses on the 20CrMnTi high strength gear process and the quality of the performance test, heat treatment was discussed. In this paper not only describes the chemical composition of 20CrMnTi and its effect on the structure and properties of gear organization, also introduced the conventional heat treatment process. Through the analysis of 20CrMnTi high strength gear just heat treatment process, heat treatment and quenching and tempering by, and in the process of adopting reasonable precautions to prevent gear defects, make the materials with comprehensive and good mechanical properties and conform to the standard, so as to meet the requirements of the use of the performance of gear.
Keywords: High strength gear，20CrMnTi，Heat treatment process，Defect
目录
一、引言· 7
二、前言· 7
（一）齿轮的发展史· 7
（二）20CrMnTi简介· 8
（三）研究的目的和意义· 8
三、方案· 9
（一）原材料的选择· 9
（二）齿轮的性能要求· 9
1. 满足齿轮材料的机械性能· 9
2. 满足齿轮材料的工艺性能· 9
3. 满足齿轮材料经济性能· 10
四、热处理· 10
（一）预备热处理· 10
（二）调质· 11
五、渗碳热处理工艺· 11
（一）钢的化学成分· 12
（二）渗碳工艺· 13
六、淬火低温回火· 13
(一) 淬火· 13
(二) 低温回火· 13
七、热处理后的金相组织· 14
(一) 20CrMnTi等温正火后金相组织· 14
(二) 20CrMnTi经渗碳后淬火、回火处理金相组织· 14
八、质量控制与检验方法· 16
(一) 随炉试样检验· 16
(二) 齿轮热处理质量检验· 19
九、热处理工艺过程中的质量检验· 19
(一) 渗碳淬火后齿轮的检验项目、内容和要求· 19
(二) 渗碳齿轮的常见缺陷及防止措施· 20
(三) 渗碳淬火后畸变原因分析及解决措施· 22
十、结论· 27
参考文献· 28
参考文献：
【1】彭福泉主编，金属材料实用手册，机械工业出版社，1987年
【2】河北工学院王健安主编，金属学与热处理下册热加工专业用，机械工业出版社，1980年
【3】中国机械工程学会热处理专业学会《热处理手册》编委会编，热处理手册第2版第二卷典型零件的热处理，机械工业出版社，1991年
【4】夏立芳编，金属热处理工艺学修订版，哈尔滨工业大学出版社，2008年
【5】热处理工艺学，机械工业出版社， 1988
【6】陆兴热，处理工程基础，北京：机械工业出版社，1997(3),30-36
【7】刘瑞堂，机械零件失效分析，哈尔滨：哈尔滨工业大学出版社，2005
【8】张太昌，齿轮检测500问，北京中国标准出版社，2007
【9】金荣植，齿轮的热处理畸变、裂纹与控制方法，机械工业出版社2014
【10】那顺桑，金属热处理300问，北京工业出版社2007
【11】金荣植，齿轮热处理常见缺陷分析与对策，化学工业出版社2014
【12】吉泽升，热处理炉，哈尔冰工业大学出版社2010
http://www.bysj580.com/