柴油机共轨高速钢金相检验方法探讨
摘要：根据柴油机共轨高速钢，以W18Cr4V为例，进行金相检测方法的探索。金相检测的一般过程：首先需将待检测的材料或零件制成金相试样，然后利用各种分析仪器对试样的内部组织进行观察和检测，必要时还可以利用显微摄影将所观察到的组织特征拍摄记录下来。
关键词：W18Cr4V 进项检测 取样 研磨 显微组织
Discussion on the common rail diesel engine of high speed steel metallographic examination method
Abstract: according to the common rail diesel engine of high speed steel, taking W18Cr4V as an example, to explore the metallographic detection method. The general process of metallographic test: first of all need to be detected material or parts made of the metallographic sample, then using a variety of analytical instruments of the samples were observed and detected the internal organization, organization characteristics when necessary, can also use the observed microscopic photography will be recorded.
Keywords: detection sampling polishing microstructure of W18Cr4V input
一、选题简介、意义
金相检测也称为金相分析，就是对金属材料的宏观组织或内部显微组织进行检测。
金属材料的组织直接影响材料本身和机械零件的性能与使用寿命。因此，金相检测在金属材料的生产和机械制造过程中应用十分广泛，是评定和控制金属材料及机械零件内在质量的重要手段。
根据柴油机共轨高速钢，以W18Cr4V为例，进行金相检测方法的探索。
二、课题综述
金相检测的一般过程：首先需将待检测的材料或零件制成金相试样，然后利用各种分析仪器对试样的内部组织进行观察和检测，必要时还可以利用显微摄影将所观察到的组织特征拍摄记录下来。
首先，去图书馆查阅W18Cr4V金相检测这方面的资料，从中收集对论文有帮忙的知识，进行整合分析。
第二，根据从图书馆查阅的资料，做相关的试验，取样与镶嵌，试样的研磨，金相显微组织的显示。
最后通过把图书馆查阅的资料和做相关的试验这些数据进行整理、分析，最后得出W18Cr4V最佳的金相检测方法：
1、取样与镶嵌：包括试样的选择、试样的截取、试样的镶嵌
2、试样的研磨：包括试样的磨平、试样的磨光、试样的抛光
金相显微组织的显示：包括化学侵蚀法、电解侵蚀法、干涉层法
三、设计（论文）体系、结构（大纲）
绪论
一、W18Cr4V材料分析
（一）合金元素对钢性能的影响
（二）合金元素的存在形式
（三）合金元素对铁碳平衡相图的影响
（四）合金元素对调质钢机械性能的影响
(五）钢中的主要合金元素的作用
二、金相试样的制备
（一）取样与镶嵌
（二）试样的研磨
（三）金相显微组织的显示
三、金相检测的方法
（一） 普通金相显微镜检测
（二） 特殊光学金相检测方法
（三） 电子显微分析
四、结论
五、参考文献
摘要：根据柴油机共轨高速钢，以W18Cr4V为例，进行金相检测方法的探索。金相检测的一般过程：首先需将待检测的材料或零件制成金相试样，然后利用各种分析仪器对试样的内部组织进行观察和检测，必要时还可以利用显微摄影将所观察到的组织特征拍摄记录下来。
关键词：W18Cr4V 进项检测 取样 研磨 显微组织
Discussion on the common rail diesel engine of high speed steel metallographic examination method
Abstract: according to the common rail diesel engine of high speed steel, taking W18Cr4V as an example, to explore the metallographic detection method. The general process of metallographic test: first of all need to be detected material or parts made of the metallographic sample, then using a variety of analytical instruments of the samples were observed and detected the internal organization, organization characteristics when necessary, can also use the observed microscopic photography will be recorded.
Keywords: detection sampling polishing microstructure of W18Cr4V input
一、选题简介、意义
金相检测也称为金相分析，就是对金属材料的宏观组织或内部显微组织进行检测。
金属材料的组织直接影响材料本身和机械零件的性能与使用寿命。因此，金相检测在金属材料的生产和机械制造过程中应用十分广泛，是评定和控制金属材料及机械零件内在质量的重要手段。
根据柴油机共轨高速钢，以W18Cr4V为例，进行金相检测方法的探索。
二、课题综述
金相检测的一般过程：首先需将待检测的材料或零件制成金相试样，然后利用各种分析仪器对试样的内部组织进行观察和检测，必要时还可以利用显微摄影将所观察到的组织特征拍摄记录下来。
首先，去图书馆查阅W18Cr4V金相检测这方面的资料，从中收集对论文有帮忙的知识，进行整合分析。
第二，根据从图书馆查阅的资料，做相关的试验，取样与镶嵌，试样的研磨，金相显微组织的显示。
最后通过把图书馆查阅的资料和做相关的试验这些数据进行整理、分析，最后得出W18Cr4V最佳的金相检测方法：
1、取样与镶嵌：包括试样的选择、试样的截取、试样的镶嵌
2、试样的研磨：包括试样的磨平、试样的磨光、试样的抛光
金相显微组织的显示：包括化学侵蚀法、电解侵蚀法、干涉层法
三、设计（论文）体系、结构（大纲）
绪论
一、W18Cr4V材料分析
（一）合金元素对钢性能的影响
（二）合金元素的存在形式
（三）合金元素对铁碳平衡相图的影响
（四）合金元素对调质钢机械性能的影响
(五）钢中的主要合金元素的作用
二、金相试样的制备
（一）取样与镶嵌
（二）试样的研磨
（三）金相显微组织的显示
三、金相检测的方法
（一） 普通金相显微镜检测
（二） 特殊光学金相检测方法
（三） 电子显微分析