15MnVN钢焊接冷裂纹及防治措施探讨
摘要：科学的不断进步和激烈的市场竞争，不仅推动着焊接技术的发展，而且危害极大，在焊接过程中焊接裂纹是焊接中的最常见的缺陷之一。它具有尖锐的缺口和大的长宽比特征，裂纹是可以引发灾难性事故的危害最大的一类缺陷。金属构件如果存在焊接裂纹，将直接影响到产品的质量和性能，因此不断减少和避免焊接裂纹便成为焊接者们孜孜以求得永恒主题之一。
关键词： 焊接 焊接裂纹
15 MnVN steel welding cold cracking and prevention measures
Abstract:Scientific progress and fierce market competition, not only to promote the development of welding technology, but also great harm in the process of welding,welding crack is one of the most common defects in welding. It has a sharp notchcharacteristic ratio and large length to width, crack is the most harmful defects cancause catastrophic accidents. Metal component if there is crack, will directly affect thequality and performance of products, therefore, continue to reduce and avoid thewelding crack has become the eternal theme of diligently strive after welding are one of.
Key words ： Welding Welding crack
一、选题简介、意义
15MnVN钢属于碳素结构钢。这类结构钢具有高强度和很好的综合机械性能，大量用于压力容器和重要的金属结构上。本文对15MnVN钢的焊接性和焊接缺陷加以分析研究，并提出一些解决办法。
二、课题综述（课题研究，主要研究的内容，要解决的问题，预期目标，研究步骤、方法及措施等）
课题研究：15MnVN钢焊接冷裂纹及防治措施探讨。
主要研究内容：15MnVN钢的的基本性能与焊接出现的裂纹处理及防治措施。
预期目标：分析出针对15MnVN钢的焊接裂纹冷处理的方法，再加以讨论出防治措施。
研究步聚、方法及措施:第一步先查阅资料了解15MnVN钢的化学成分、基本性能、应用，了解此钢焊接会出现什么样的缺陷，其次再查阅焊接裂纹冷处理的相关知识，最后查阅此钢的焊接裂纹如何冷裂纹处理及防治措施。
参考文献
[1]：焊接方法与设备.雷世明主编，机械工业出版社，1999
[2]：熔焊原理及金属材料焊接.应若菜主编，机械工业出版社，2000
[3]：弧焊电源.郑宜庭等编，机械工业出版社，1990
[4]：焊接实训.杨兵兵主编，高等教育出版社，2009
[5]：焊接材料简明选用手册.张子荣等编著，机械工业出版社，1999
[6]：焊接工艺人员手册.俞尚知主编，上海科学技术出版社，1991
[7]：电弧.周玉生主编，机械工业出版社，1994
[8]：焊接手册.美国焊接学会编，机械工业出版社，1988
9].焊接自动控制基础：赵家瑞等编，机械工业出版社，1990
10].金属结构的电弧焊：天津大学编，机械工业出版社，1993
摘要：科学的不断进步和激烈的市场竞争，不仅推动着焊接技术的发展，而且危害极大，在焊接过程中焊接裂纹是焊接中的最常见的缺陷之一。它具有尖锐的缺口和大的长宽比特征，裂纹是可以引发灾难性事故的危害最大的一类缺陷。金属构件如果存在焊接裂纹，将直接影响到产品的质量和性能，因此不断减少和避免焊接裂纹便成为焊接者们孜孜以求得永恒主题之一。
关键词： 焊接 焊接裂纹
15 MnVN steel welding cold cracking and prevention measures
Abstract:Scientific progress and fierce market competition, not only to promote the development of welding technology, but also great harm in the process of welding,welding crack is one of the most common defects in welding. It has a sharp notchcharacteristic ratio and large length to width, crack is the most harmful defects cancause catastrophic accidents. Metal component if there is crack, will directly affect thequality and performance of products, therefore, continue to reduce and avoid thewelding crack has become the eternal theme of diligently strive after welding are one of.
Key words ： Welding Welding crack
目录
前言 1
第一章 焊接冷裂纹的危害及分类 2
1.1 焊接冷裂纹的危害 2
1.2 焊接冷裂纹的分类 2
第二章15MnVN钢的化学成分、基本性能、应用 3
2.1 15MnVN钢的化学成分 3
2.2 15MnVN钢的基本性能、应用 3
第三章 分析15MnVN钢焊接的工艺性 4
第四章 冷裂纹的基本特征 4
第五章15MnVN钢形成冷裂纹的基本因素及其作用 7
5.1形成冷裂纹的基本因素及其作用 7
5.2基本因素的作用 9
5.2.1 焊接冷裂纹的形态和特征 9
第六章 防止冷裂纹的措施 10
6.1 选择冷裂纹敏感性低的材料 10
6.2冷裂纹产生的原因及预防措施 10
6.2.1 冷裂纹产生的原因 10
6.2.2 冷裂纹的预防措施 10
6.3 焊前预热 10
6.3.1 坡口制备 10
6.3.2 焊接方法选用 11
6.3.3 焊接位置与焊枪角度 12
6.3.4 预热温度及焊接线能量 12
6.3.5 焊接参数 12
6.4 其他焊接缺陷及预防措施 12
6.4.1 热裂纹 12
6.4.2脆化 13
6.4.3气孔 14
第七章 结论 15
参考文献 17
致谢 18
一、选题简介、意义
15MnVN钢属于碳素结构钢。这类结构钢具有高强度和很好的综合机械性能，大量用于压力容器和重要的金属结构上。本文对15MnVN钢的焊接性和焊接缺陷加以分析研究，并提出一些解决办法。
二、课题综述（课题研究，主要研究的内容，要解决的问题，预期目标，研究步骤、方法及措施等）
课题研究：15MnVN钢焊接冷裂纹及防治措施探讨。
主要研究内容：15MnVN钢的的基本性能与焊接出现的裂纹处理及防治措施。
预期目标：分析出针对15MnVN钢的焊接裂纹冷处理的方法，再加以讨论出防治措施。
研究步聚、方法及措施:第一步先查阅资料了解15MnVN钢的化学成分、基本性能、应用，了解此钢焊接会出现什么样的缺陷，其次再查阅焊接裂纹冷处理的相关知识，最后查阅此钢的焊接裂纹如何冷裂纹处理及防治措施。
参考文献
[1]：焊接方法与设备.雷世明主编，机械工业出版社，1999
[2]：熔焊原理及金属材料焊接.应若菜主编，机械工业出版社，2000
[3]：弧焊电源.郑宜庭等编，机械工业出版社，1990
[4]：焊接实训.杨兵兵主编，高等教育出版社，2009
[5]：焊接材料简明选用手册.张子荣等编著，机械工业出版社，1999
[6]：焊接工艺人员手册.俞尚知主编，上海科学技术出版社，1991
[7]：电弧.周玉生主编，机械工业出版社，1994
[8]：焊接手册.美国焊接学会编，机械工业出版社，1988
9].焊接自动控制基础：赵家瑞等编，机械工业出版社，1990
10].金属结构的电弧焊：天津大学编，机械工业出版社，1993