起重机齿轮的失效分析及生产制造
摘 要：起重机齿轮传动是目前最重要也是应用最广泛的一种传动形式。由于齿轮在传动过程中受到各种因素导致起重机齿轮失效。起重机齿轮失效直接影响着力学性能的发挥，需要去解决，解决这些问题才能对起重机齿轮的生产制造起着重要的作用。本文首先进行了齿轮的失效分析，首先介绍起重机齿轮的失效分析，这是围绕了起重机齿轮的失效特征及其失效原因进行分析的，并且对起重机齿轮的失效形式采取了预防措施，这样对后期的生产制造奠定了良好的基础。其中举例选用了双联圆柱齿轮进行加工制造，并且选用的是范成法来完成生产制造的，以上就是本文所要阐述的内容。
关键词：失效分析；生产制造；加工方法
Failure analysis and manufacture crane gear
Abstract:Crane gear drive is the most important and the most widely used. Because the gears in the transmission process by all kinds of factors cause the crane gear failure. Failure will directly affect the mechanical properties of the play crane gear, need to solve the problem, to solve these problems in order to crane gear manufacturing plays an important role. This paper first has carried on the analysis of gear failure, first introduces the failure analysis of crane gear, which is around the crane gear failure characteristics and failure analysis, and the failure forms of the crane gear to take preventive measures, so that the post production has laid a good foundation. For example, the use of double cylindrical gear manufacturing, and selected Fan Cheng fa to complete the production, the article describes the contents of the.
Keywords：analysis of gear,manufacture crane，Processing method
摘 要：起重机齿轮传动是目前最重要也是应用最广泛的一种传动形式。由于齿轮在传动过程中受到各种因素导致起重机齿轮失效。起重机齿轮失效直接影响着力学性能的发挥，需要去解决，解决这些问题才能对起重机齿轮的生产制造起着重要的作用。本文首先进行了齿轮的失效分析，首先介绍起重机齿轮的失效分析，这是围绕了起重机齿轮的失效特征及其失效原因进行分析的，并且对起重机齿轮的失效形式采取了预防措施，这样对后期的生产制造奠定了良好的基础。其中举例选用了双联圆柱齿轮进行加工制造，并且选用的是范成法来完成生产制造的，以上就是本文所要阐述的内容。
关键词：失效分析；生产制造；加工方法
Failure analysis and manufacture crane gear
Abstract:Crane gear drive is the most important and the most widely used. Because the gears in the transmission process by all kinds of factors cause the crane gear failure. Failure will directly affect the mechanical properties of the play crane gear, need to solve the problem, to solve these problems in order to crane gear manufacturing plays an important role. This paper first has carried on the analysis of gear failure, first introduces the failure analysis of crane gear, which is around the crane gear failure characteristics and failure analysis, and the failure forms of the crane gear to take preventive measures, so that the post production has laid a good foundation. For example, the use of double cylindrical gear manufacturing, and selected Fan Cheng fa to complete the production, the article describes the contents of the.
Keywords：analysis of gear,manufacture crane，Processing method
目录
引言 1
1、起重机齿轮的失效分析 1
1.1起重机齿轮的轮齿折断失效分析 1
1.2起重机齿轮的齿面点蚀失效分析 2
1.3起重机齿轮的齿面胶合失效分析 3
1.4起重机齿轮的齿面磨损失效分析 4
1.5 ．起重机齿轮的塑性变形失效分析 5
1.6 起重机齿轮的其他的失效形式分析 6
2、起重机齿轮的生产制造 7
2.1齿轮材料的选择 7
2.2双联圆柱齿轮 9
2.3齿坯制造 10
2.4齿坯热处理 10
2.5齿坯精加工 11
2.6轮齿加工 12
2.7轮齿热处理 14
2.8齿轮定位面的精加工 15
2.9轮齿的精加工 16
3、结论 17
参考文献： 19
首先指出了起重机齿轮失效的特征析和齿轮失效产生的原因以及一些各自失效形式预防措施，其中起重机齿轮的失效原因可以总结为两大类就是起重机齿轮齿面的失效和起重机齿轮的整体失效，其中起重机齿轮的齿面失效和起重机齿轮整体的失效都包括很多种形式。例如，轮齿折断和塑性变形就是起重机齿轮整体的失效，而齿面点蚀（表面疲劳磨损）、齿面磨粒磨损和齿面胶合则是齿轮齿面的失效分析。
接着通过了上面的失效分析，选择起重机上的一种双联圆柱齿轮进行生产加工制造，起重机齿轮的的生产制造有很多种方法，双联圆柱齿轮使用的是范成法也称作是展成法或者是包络法，是目前常用的一种方法，它是利用两个齿轮的啮合是其共轭齿廓互为包络线的原理来实现切割的。起重机中的齿轮模数大，大多采用调质处理和滚齿或者是插齿工艺。本文围绕的是双联圆柱齿轮的加工方法，它的加工工艺流程是：齿轮材料的选择-双联圆柱齿轮-齿坯制造-齿坯热处理-齿坯精加工-轮齿加工-轮齿热处理-齿轮定位面的精加工-轮齿的精加工。
参考文献：
[1] 徐灏.机械设计手册[M].第2版.北京：机械工业出版社,2003
[2] 张建中.机械设计基础[M].第1版.徐州：中国矿业大学出版社,1999
[3] 杨黎明.机械原理及机械零件[M].第1版.北京：高等教育出版社,1988
[4] 陈立德.机械设计基础[M].北京：高等教育出版社,2000
[5] 黄华梁，彭文生.机械设计基础[M].第3版.北京：高等教育出版社,2001
[6] 郭仁生.机械设计基础[M].北京：清华大学出版社,2001
[7] 武友德，苏珉.机械加工工艺[M].北京：北京理工大学出版社，2011
[8] 刘力.机械制图[M].北京：高等教育出版社，2001
[9] 王杰英.金属工艺学[M].北京：高等教育出版社，2000
[10] 李翠梅，王俊伟.工程力学与机械设计基础[M].北京：北京师范大学出版社，2010